Sci Total Environ吴龙华:NMT验证铝毒削弱景天镉积累能力 | NMT重金属创新科研平台

 楼主| xuyue_2017 发表于 2020-6-30 16:05  
查看: 5568|回复: 0|显示全部楼层 |阅读模式
NMT作为生命科学底层核心技术,是建立活体创新科研平台的必备技术。2005~2020年,NMT已扎根中国15年。2020年,中国NMT销往瑞士苏黎世大学,正式打开欧洲市场。

研究使用平台:NMT重金属创新科研平台
期刊:Science of the Total Environment
主题:NMT验证铝毒削弱景天镉积累能力
标题:Aluminum toxicity decreases thephytoextraction capability by cadmium/zinc hyperaccumulator Sedumplumbizincicola in acid soils
影响因子:5.589
检测指标:Cd2+流速
检测样品:伴矿景天
Cd2+流实验处理方法:
伴矿景天幼苗在Al浓度为0200400μMpH4的环境下处理212244872小时
Cd2+流实验测试液成份:
50 μM CdCl2,0.1 mM CaCl2, MgCl2 and KCl, 1.0 mM NaCl, pH 4.00
作者:中科院南京土壤所吴龙华、李柱、周嘉文
中文摘要(谷歌机翻)
在酸性土壤中过量的铝(Al)或在重复的植物提取过程中由于酸化而释放的Al可能会损害超级蓄积剂的植物提取效率,但这通常被忽略。
在这里,我们首次在长期(7周)和短期(72小时)以及土壤条件下,通过水培试验研究了Al对镉(Cd)和锌(Zn)超积累性景天(Sedum plumbizincicola)的毒性。锅实验。在长期的水培试验中,即使在pH值为5.00<100μMAl下(可溶性Al8.74μM),也发现Al的可观察到的毒性作用,与无Al处理相比,它能降低芽Cd吸收39.3%。
非损伤微测技术显示,在48小时后用200μMAlpH 4.00条件下处理后,根Cd2 +的流入被显着抑制。盆栽实验证实,Al毒性可抑制酸性土壤中植物的生长和金属吸收,可交换的Al0.33 cmolc kg-1Al胁迫引起的根部表面Cd吸附的减少可能是导致枝条Cd吸收减少的重要因素。
对金属化学形态的分析表明,铝的添加显着影响茎中CdZn的化学形态,使它们的活动性降低,从而限制了CdZn的转运。
在酸性土壤中和在反复的植物提取过程中,土壤中可能发生的铝毒害是限制使用超级蓄积剂从污染土壤中去除金属的效率的主要因素。

                                                                  


Net fluxes of Cd2+ at the root surface S.plumbizincicola under Al exposure in the short term. The error bars are SE, n =8. Different letters indicate significant differences under different Altreatments at the same exposure time at P < 0.05.
英文摘要
Excessive aluminum(Al) in acid soils or Al released due to acidification during repeatedphytoextraction might impair the phytoextraction efficiency ofhyperaccumulators but this is often neglected.
Here, weinvestigate for the first time the toxicity of Al to the cadmium (Cd) and zinc(Zn) hyperaccumulator Sedum plumbizincicola with hydroponics experiments bothin the long (7 weeks) and short terms (72 hours), and in soil conditions in apot experiment. In the long-term hydroponics experiment, observable toxiceffects of Al were found even at < 100 μM Al at pH 5.00 (soluble Al: 8.74μM) which lowered shoot Cd uptake by 39.3% compared with the Al-free treatment.
Non-invasiveMicro-test Technology shows that root Cd2+ influx was significantlyinhibited after treatment with 200 μM Al at pH 4.00 after 48 hours. The potexperiment confirms that Al toxicity induced inhibition of plant growth andmetal uptake in the acid soil with an exchangeable Al of 0.33 cmolc kg−1.Decreasing Cd adsorption at root surfaces induced by Al stress may be animportant factor in declining shoot Cd uptake.
Analysis of thechemical forms of metals shows that Al addition significantly influenced thechemical forms of Cd and Zn in stems, made them less mobile and thus restrainedCd and Zn translocation.
Aluminum toxicitythat potentially occurs in acid soils and in soils during repeatedphytoextraction would be a primary factor limiting metal removal efficiencyfrom contaminated soils using hyperaccumulators.
关键词:非损伤微测技术,Cd2+流速,植物重金属



Sci Total Environ吴龙华:NMT验证铝毒削弱景天镉积累能力 | NMT重金属创新科研平台

本帖子中包含更多资源

您需要 登录 才可以下载或查看,没有帐号?注册新帐号

x
您需要登录后才可以回帖 登录 | 注册新帐号

本版积分规则  | 请遵守小木虫学术科研第一站管理条例,不得违反国家法律法规

Copyright © 2014-2020 小木虫学术科研第一站(xmuchong.com)All Rights Reserved.

公安备案:津公网安备 12011102000110号

     

ICP备案/许可证号:津ICP备14003772号-3

     

跟帖评论自律管理承诺书

    

优质网站认证编号:NO.00120190822002WZ

     © 2014-2020 小木虫学术科研第一站

快速回复 返回顶部 返回列表